二氧化碳加氢直接合成二甲醚催化剂的研究——沉淀次序对复合催化剂结构和性能的影响

以草酸乙醇溶液为沉淀剂,采用不同的沉淀次序(并流、反加和正加)制备了CuO-ZnO-Al2O3/HZSM-5复合型催化剂,对CO2加氢直接合成二甲醚反应的催化活性顺序为:并流法催化剂>反加法催化剂>正加法催化剂。3种复合催化剂的还原温度由低到高的顺序为:并流法催化剂<反加法催化剂<正加法催化剂。在沉淀过程中,反加法和正加法均形成类胶体沉淀,相应催化剂的比表面积也较大。IR研究发现,催化剂在1101cm-1处表现Cu/Zn/Al氧化物与HZSM-5分子筛之间相互作用的IR吸收峰强度与其催化活性间存在对应关系。XRD结果表明,并流法得到的催化剂前驱体中有铜锌同形取代现象,有利于催化剂活性的发挥。     

无皂型乳液聚合的研究进展

综述了无皂型乳液聚合反应机理及影响乳液稳定性的因素。对无皂型乳液聚合制备方法进行了论述，并介绍了无皂型乳液聚合的研究动态、应用和发展前景。     

双膦胺镍-甲基铝氧烷体系催化苯乙烯聚合

研究了具有新型结构的双膦胺镍配合物N,N-双(二苯膦基)-对甲氧基苯胺二氯化镍-甲基铝氧烷(PNP-N i-MAO)催化体系对苯乙烯聚合的催化性能,考察了聚合温度、n(A l)∶n(PNP-N i)、PNP-N i的浓度和苯乙烯的浓度对催化活性、苯乙烯转化率、聚苯乙烯相对分子质量及其分布的影响,并用核磁共振和凝胶色谱对聚苯乙烯的结构进行了表征。实验结果表明,在聚合温度25℃、聚合时间1h、n(A l)∶n(PNP-N i)=300、c(苯乙烯)=2.3m ol/L、c(PNP-N i)=0.4mm ol/L、甲苯为溶剂的适宜条件下,苯乙烯的转化率可达95%以上,催化活性达到5×105g/(m ol.h)左右。核磁共振和凝胶色谱表征结果显示,所得聚苯乙烯为无规结构,重均相对分子质量约为1×104,相对分子质量分布Mw/Mn约为2。     

Ring‐opening polymerization of lactones initiated by diphenylzinc–coinitiator systems

Diphenylzinc, alone or in combination with water and butanone as coinitiators, was used as a polymerization initiator system for a variety of lactones at varying temperatures. The resulting data indicate that the course of the polymerization is greatly influenced by the lactone structure, as well as by the molar ratio of coinitiator to diphenylzinc. When used alone, diphenylzinc exhibited high activity as an initiator in δ‐valerolactone polymerizations, although it was less efficient when used in the β‐butyrolactone and the β‐propiolactone polymerizations. Activity in the polymerization of β‐lactones was increased by adding small amounts of butanone or water. It was also observed that the diphenylzinc–butanone combination was more effective than the diphenylzinc–water mixture in the polymerizations of β‐butyrolactone and β‐propiolactone. Copyright © 2003 Society of Chemical Industry     

FCC汽油叠合生产柴油的研究——(Ⅰ)叠合催化剂的研制

采用中孔γ-Al2O3为载体，以非贵金属Ni为活性金属组分，以金属Sn为助剂组分，制备了FCC汽油叠合生产柴油的催化剂。在实验室小型连续流动式固定床装置上，以FCC汽油为原料，考察了主活性金属负载量、助催化剂、催化剂制备条件对催化剂性能的影响。研究结果表明，在活性金属Ni质量分数为8％，助催化剂Sn质量分数为1％，浸渍时间6h，焙烧温度500℃，焙烧时间4h的条件下，制备的叠合催化剂的催化性能最好。并对催化剂进行了1500h的稳定性试验和再生性能考察，结果表明该叠合催化剂具有良好的稳定性和再生性能。     

Monte Carlo simulation of gas phase polymerization of 1,3‐butadiene. Part II: Kinetics optimization and confirmation

Studies on the deactivations and initiations of gas phase polymerizations of 1,3‐butadiene have been achieved by Monte Carlo simulation. Initiation and deactivation control the reaction before and after the peak of the polymerization rate, respectively. The influence of polymerization temperature has been studied. Monte Carlo modeling of polymerization kinetics and mechanism was confirmed by the agreement of experimental data and simulation results of polymerizations run with a temporary evacuation of monomer. The balance of catalysts and active chains is established by both initiation and chain transfer reactions with cocatalyst, which causes a ‘pseudo‐stability’ stage. © 2003 Society of Chemical Industry     

Inhibition of radical polymerization in solvent‐based systems (security of solvent‐based radical polymerization of PSA‐acrylic in a plant reactor)

This article shows the influence of some chain‐transfer agents as inhibitors for acrylic solvent‐based polymerization. These chain‐transfer agents can offer significant advantages, as outlined below. The following chain‐transfer agents were studied to stop or slow down the polymerization process in the case of a runaway: n‐dodecyl mercaptan, trimethylolpropane‐trimercaptoacetate, phenothiazine, diphenylphenylen diamine, cuprum oxide, isopropanol, toluene, and carbon tetrachloride. Synthesized pressure‐sensitive adhesive based on acrylic polymers and containing 2‐ethylhexyl acrylate, methyl acrylate, and acrylic acid were used for the production of self‐adhesives with high cohesion. The polymerization was accomplished in ethyl acetate. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 87: 1354–1357, 2003     

无机阻燃剂高聚合度聚磷酸铵的研制

以五氧化二磷、磷酸铵盐、尿素为原料、氨气为保护气,制备了高聚合度聚磷酸铵无机阻燃剂。考察了五氧化二磷、磷酸铵盐、尿素的用量和反应温度对聚磷酸铵平均聚合度的影响。采用端基滴定法测定了聚磷酸铵的聚合度,并用X射线衍射(XRD)法表征了聚磷酸铵的晶体结构,同时测定了聚磷酸铵的粒度和溶解度。实验结果表明,制备聚磷酸铵的最佳反应条件为:n(磷酸氢二铵)∶n(五氧化二磷)∶n(尿素)=1∶1∶0.3,反应温度280~300℃,反应时间40m in,热处理温度250~280℃,热处理时间110m in。在此条件下制备的聚磷酸铵的平均聚合度大于600,平均粒径直径小于50μm,在水中的溶解度小于0.4g;XRD表征结果表明,所合成的物质为Ⅱ型聚磷酸铵。     

聚甲亚胺改性尼龙6复合材料的等温结晶动力学

采用差示扫描量热法（DSC）对聚甲亚胺（PAM）/尼龙6复合材料等温结晶过程进行了研究。结果表明，PAM的加入使得基体的结晶速率增大，尤其是当含量为5%时，半结晶期明显减少。研究还发现，该体系的等温结晶过程完全可以用Avrami方程来描述，各试样的Avrami指数均在2-3之间，表明Avrami指数，球晶生长方式基本不受聚甲亚胺加入的影响。基体中原位形成的聚甲胺微纤起到了诱导结晶的作用，使得基体的结晶速率加快，但随着微纤含量的增加，由于分散性能变差而使得诱导结晶的能力减弱，表现为结晶速率又有所降低。     

砂岩酸化中水化硅沉淀的影响因素分析

讨论了砂岩酸化中产生水化硅沉淀的反应机理。使高岭土与1.0%HF和多种配比的HCl HF在不同温度(20-90℃)反应不同时间(10-300分钟),用等离子吸收光谱法(ICP)测定酸液中可溶性硅的浓度(mg/L),取某时段测定值的减小量为该时段水化硅沉淀生成量,讨论了多种因素的影响,得到了如下结果和结论。反应温度越高,则高岭土与HF之间的反应越快,形成水化硅沉淀的时间越短,最终生成的沉淀量越大;在HF中加入HCl(使用土酸体系)、减小土酸中HF质量分数、加大土酸中HCl、HF质量分数比,均可使生成沉淀时间延后,使最终生成沉淀量减少。60℃时300分钟沉淀量,在1.0%HF、5.0%HCl 1.0%HF、9.0%HCl 1.0%HF中分别为482、321、201mg/L。提出了在酸化设计与施工中可以采取的6条简便易行的减少水化硅沉淀量的措施。图4表1参6。